|Classification:||Chemical Auxiliary Agent||Usage:||Plastic Auxiliary Agents|
|Appearance:||White Powder||Initial Melting Temperature:||Initial Melting Temperature|
|Heating Loss:||0.5%||Recommended Dosage:||2PHR~7PHR|
one pack lead stabilizer,
pvc lead stabilizer
The composite lead salt heat stabilizer LC-350Q adopts the symbiotic reaction technology, mixes the three salts, the two salts and the metal soap in the reaction system with the initial ecological grain size and various lubricants to ensure the heat stabilizer full dispersion in the pvc system. At the same time, due to co-melting with the lubricant to form granules, poisoning caused by lead dust is also avoided. The composite lead salt stabilizer contains the heat stabilizer component and lubricant component required for processing, and has the following advantages:
|Product name||Lead based pvc stabilizer|
|Physical form||white flakes|
|Metal content (oxide)||35%|
|Initial melting temperature||70 ℃|
|The relative density||1.15 ± 0.5|
High lead content, suitable for the production of WPC floor
Packing and Storage:
25KG/ Woven bag
No decomposition at room temperature, but should be stored in a cool and dry place. Keep away from hot, fire source, avoid direct sunlight. Recommended storage and mixing areas have good ventilation conditions to avoid inhalation. Transportation according to the general chemicals.
Pay attention to the application area, can not be used for food contact products.